POLCO® 223 is a high-performance, multi-purpose polyurea coating designed for processing through plural component, high pressure, dispensing equipment. Once fully cured, it is tough and flexible with high impact and tear resistance, along withexcellent chemical and water resistance.

POLCO® 223 can be applied under very low ambient temperature conditions (-40F / -40ºC), in high humidity and in the presence of moisture without affecting the final properties of the material. Proper adhesion relies upon substrate dryness, preparation and compatibility.

This is photos, that Quocthang Co construct spray polyurea coating

POLCO® 223 performs well as a corrosion-resistant coating for concrete and steel applications with extreme exposure to acids, bases, salts and other corrosives.

Physical Properties (Components)       Component “A”           Component “B”

Viscosity at 75ºF (cps)                              950-1500                        350-600

Specific Gravity (gr/ml)                              1.10-1.12                       1.02-1.05

Physical Properties (Final Product)      ASTM Test Method                  Value

Hardness, Shore D,                                    ASTM D-2240                           60

Tensile Strength (psi),                                 ASTM D-412                        3400

Elongation (%),                                             ASTM D-412                          150

Tear Strength (pli),                                      ASTM D-624, Die C                480

Colour                                                                                            Black or Neutral

Service Temperature                                                                    -40^oF to 200^oF

Bond strength                                      Substrate               Pull off strength N/mm2 (Mpa)

Concrete                                  2.9

Steel                                        2.5

Wood                                      3.4

Handling Characteristics

Mix Ratio by Volume (Component A/ Component B)                            1:1

Gel Time (at 130-150oF), (seconds)                                                        3

Tack Free Time (seconds)                                                                       15

Demold Time (minutes)                                                                           20

Final Cure Time (hours)*                                                                          24

(*) Due to nature of the product final physical properties will be reached in a course of several days.

Storage

Components A and B should be kept well sealed in a dry place at a temperature between 75ºF and 90ºF (23ºC-32ºC). Purge opened containers with dry nitrogen before resealing. Component B requires thorough mixing prior to each use/application.  For more information refer to the product MSDS.

Packaging

Component A:               55 gallons steel drum (closed top)                     490 lb Net Weight

Component B:               55 gallons steel drum (open top)                        445 lb Net Weight

Important: This information is believed to be accurate but is given without acceptance of liability, expressed or implied, except that it is accurate to the best knowledge of Polco Australia Pty Ltd. The data on these sheets relates only to the specific material designated herein. Polco Australia Pty Ltd assumes no legal responsibility or liability for use or reliance upon this data. The user should conduct sufficient investigation to establish the suitability of any product for its intended use.